Flexible Thermoelectric Devices of Ultrahigh Power Factor by Scalable Printing and Interface Engineering

journal contribution
posted on 2020-04-03, 00:00 authored by Chaochao Dun, Chinathambi Karthik, Courtney Hollar, David Estrada, Joseph Richardson, Mortaza Saeidi-Javash, Nicholas Kempf, Yanliang Zhang
Printing is a versatile method to transform semiconducting nanoparticle inks into functional and flexible devices. In particular, thermoelectric nanoparticles are attractive building blocks to fabricate flexible devices for energy harvesting and cooling applications. However, the performance of printed devices are plagued by poor interfacial connections between nanoparticles and resulting low carrier mobility. While many rigid bulk materials have shown a thermoelectric figure of merit ZT greater than unity, it is an exacting challenge to develop flexible materials with ZT near unity. Here, a scalable screen-printing method to fabricate high-performance and flexible thermoelectric devices is reported. A tellurium-based nanosolder approach is employed to bridge the interfaces between the BiSbTe particles during the postprinting sintering process. The printed BiSbTe flexible films demonstrate an ultrahigh room-temperature power factor of 3 mW m−1 K−2 and ZT about 1, significantly higher than the best reported values for flexible films. A fully printed thermoelectric generator produces a high power density of 18.8 mW cm−2 achievable with a small temperature gradient of 80 °C. This screen-printing method, which directly transforms thermoelectric nanoparticles into high-performance and flexible devices, presents a significant leap to make thermoelectrics a commercially viable technology for a broad range of energy harvesting and cooling applications.

History

Date Modified

2020-04-03

Language

  • English

Alternate Identifier

16163028

Publisher

Advanced Science News

Usage metrics

    Integrated Imaging Facility

    Categories

    No categories selected

    Keywords

    Exports

    RefWorks
    BibTeX
    Ref. manager
    Endnote
    DataCite
    NLM
    DC